ASTM A792(M)-2001 Free Samples Price Hot-Rolled Prepainted Galvalume Coil

More Views

ASTM A792(M)-2001 Free Samples Price Hot-Rolled Prepainted Galvalume Coil

  • FOB Price: 600-1000 USD / ton
  • MOQ: 1 ton
  • Supply Capability: 5000 ton / month
  • Port: Tianjin/Qingdao/Shanghai Port
  • Delivery: 15-30days
  • Packaging: Bundles/Lifting belts/Plastic caps/Waterproof cloth/Customers requirment

Details

General Description

55% Al Zinc (Galvalume)steel coil is is a hot dipped zinc /aluminium alloy coated steel with cold rolled steel coil of various strengths and thicknesses as base material and with regular spangle surface. It made by 55% Al, 43.4% Zinc and 1.6% Si at the high temperature of 600℃, and its entire structure of aluminium-ferrum-silicon-zinc , which forms a alloy of compact four element crystal. have the excellent performance of corrosion resisting and heat reflection and economy.

Applications 

*Construction

Roofing, Doors&Windows,Roller Shutter Door, Framework ect.

*Home Appliance

Refrigerator Pedestal, Refrigerated storage, Kitchen Equipment ect

*Automotive& Boats Industry

Body Shell, Pedestal, Oil tank ect

*Base Material of Colored Coated Coil


Comparison of Galvanized and Galvalume

1.Corrosion Resistance

 Atmospheric exposure test results throughout world, proved that under the condition of same coating thickness, the corrosion resistance of 55% AL Zinc steel coil is higher 3-6 times than galvanized steel coil.

2.Resistance to high temperatures.

Comparison of 55%Al Zinc steel coil and galvanized steel coil,

55% Al Zinc steel coil have excellent high temperature oxidation and heat reflection. And have certain heat resistance. Normally, the appearance does not change significantly at 300 degrees temperatures.

Maximum use temperature(Appearance Nondiscoloration ):

1) Galvanized steel coil: 230℃.  

2) 55% Al Zinc steel coil: 316℃.

3. Heat reflection

The heat reflection of 55% Al  Zinc steel coil is better than galvanized steel coil. Which can reflect 80% of heat energy in sunlight. For cladding and roofing . can achieve energy saving effect.  

4. Formability

55% Al Zinc alloy coating has a higher hardness than zinc coating, but it have strong adhesion to base material. So as long as it is operated according to the regulations. It can obtain the same formability as galvanized steel coil.

5. Paintability

55% Al Zinc steel coil is most suitable for coating applications. It is unique coating organization can provide excellent coating adhesion and good ductility. Provide the most outstanding performance.

6. Weldability

55% Al Zinc coating have 55% Al content. The welding conditions more strict than galvanized steel coil. 


Chemical Composition

Standard

Element  Material

Steel         Grade

C

Si

Mn

P

S

Al

Cu

Ni

Cr

Mo

V

Cb

Ti

N

 

 

 

ASTM A792(M)

CS type A

0.10

--

0.6

0.03

0.035

--

0.25

0.20

0.15

0.06

0.008

0.008

0.025

-

CS type B

0.02-0.15

--

0.6

0.03

0.035

--

0.25

0.20

0.15

0.06

0.008

0.008

0.025

-

CS type C

0.08

--

0.6

0.10

0.035

--

0.25

0.20

0.15

0.06

0.008

0.008

0.025

-

FS

0.02-0.10

--

0.5

0.02

0.030

--

0.20

0.20

0.15

0.06

0.008

0.008

0.025

-

DS

0.06

--

0.5

0.02

0.025

0.01min

0.20

0.20

0.15

0.06

0.008

0.008

0.025

-

Grade 33 (Gr.230)

0.20

--

1.35

0.04

0.04

--

0.25

0.20

0.15

0.06

0.008

0.008

0.025

-

Grade 37 (Gr.255)

0.20

--

1.35

0.10

0.04

--

0.25

0.20

0.15

0.06

0.008

0.008

0.025

-

Grade 40 (Gr.275)

0.25

--

1.35

0.10

0.04

--

0.25

0.20

0.15

0.06

0.008

0.008

0.025

-

Grade 50 (Gr.340)

Class 1  Class 2  Class 3

0.25

--

1.35

0.20

0.04

--

0.25

0.20

0.15

0.06

0.008

0.008

0.025

-

Grade 80 (Gr.550) Class 1

0.20

--

1.35

0.04

0.04

--

0.25

0.20

0.15

0.06

0.008

0.015

0.025

-

Grade 80 (Gr.550) Class 2

0.02

--

1.35

0.05

0.02

--

0.25

0.20

0.15

0.06

0.1

0.1

0.15

-

 

Mechanical Properties


Standard

 

Steel Grade

Yield   Strength

Tensile  Strength

 

Elongation %

Min  Ksi (Mpa)

Min  Ksi (Mpa)

 

 

 

 

 

ASTM A792(M)

CS type A

30/60(205/410)

--

≥20

CS type B

35/60(245/410)

--

≥20

CS type C

35/65(205/450)

--

≥15

FS

25/40(170/275)

--

≥24

DS

20/35(140/240)

--

≥30

Grade 33 (Gr.230)

33(230)

45(310)

≥20

Grade 37 (Gr.255)

37(255)

52(360)

≥18

Grade 40 (Gr.275)

40(275)

55(380)

≥16

Grade 50

 (Gr.340)

Class 1

50(340)

65(450)

≥12

Class2

50(340)

--

≥12

Class4

50(340)

60(410)

≥12

Grade 80 (Gr.550)

Class 1

80(550)

82(570)

--

Class2

80(550)

82(570)

--


Dimension Capability

Remark: All thickness are based material thickness(BMT).

Standard

Steel Grade

Thickness Range (mm)

Width Range(mm)

Remark

JIS3321      (cold rolled)

 

 

All Steel Grade

 

 

0.23--2.3

 

 

610--1250

 

Coil ID:508/610mm;  Coil Weight:3-7tons

ASTM A792(M)

EN10125

Coating Mass

 

Standard

 

Coating Designation

Min Average Coating Mass In Triple-Spot Test

Minimum Coating Mass At a Single Spot

Total Both Sides

Total Both Sides

      Inch-Pound Units                      Unit:oz/ft2

 

ASTM A792(M)

AZ50

0.5

0.43

AZ55

0.55

0.50

AZ60

0.60

0.52

                                         Si Units                            Unit: g/m2

 

ASTM A792(M)

AZM150

150

130

AZM165

165

150

AZM180

185

155

Remark: The min triple spot average coating weight mass on any one sides should not be less than 40% of the single spot requirement. 

Ratio of the inside bend diameter

Steel Grade

Ratio of the inside bend diameter to thickness of specimen(Any direction)

Grade 33 (Gr.230)

1 1/2t

Grade 37 (Gr.255)

2t

Grade 40 (Gr.275)

2 1/2

Grade 50 (Gr.340)

Class 1  Class 2  Class 3

--

Grade 80 (Gr.550)      Class 1   Class 2  

--

Remark: SS Grades 50 and 80 are not subject to bend test requirements. Angle of bend: 180degree

Remark:

1. imperfections such as small pits, variations in spangle size, dark spots, stripe marks , light passivation

stains ,stretch leveling breaks,skin pass marks,scratches, zinc run off marks are permissible on surface.

2. chemical passivation protects the surface against humidity and reduces the risk of formation of “white rust” during transportation and storage, local discolouring as a result of this treatment is permissible and does not impair the quality.

3.  Oiling also reduces the risk of corrosion of the surface.

4. Resin Coated offers additional corrosion protection by transparent organic film. Specially protection against anti-fingerprint

Package

blob.png 

Storage Transportation and Loading /unloading

Storage:

1) keep the product dry.

2) Store the product in a dry and well ventilated area preferably indoors. to avoid condensation and moisture penetration. Store the productions in a roofed storage area.

3) Don’t put the products where they could be exposed to sand and dust. If sand or dust build up on a sheet.they can damage zinc or paint coatings, sand and dust also hinder drying and thus promote white rust formation.

4) Don’s stack sheets or coils excessively high. This is important for safety as well as for the prevention of sheet deformation or other damage. Inventory terms should be as short as possible(Within 6 month)

Transport and Loading/unloading:

1) Don’t push the cut sheets or roll the coil with a forklift. Since this could cause scratching.

2) When transporting coil in a truck, care should be taken to protect the coil surfaces against damage. Using preferably. A rubber sheet beneath the coil or an exclusive transport stand.

3) When transporting coils. Firmly fix the stacked sheets so that they do not slip off due to vibration.